杜邦耐盐水腐蚀性测试.doc
【精品文档】如有侵权，请联系网站删除，仅供学习与交流杜邦耐盐水腐蚀性测试TITLE: SALT CORROSION TEST PROTOCOL耐盐水腐蚀性测试GCTMP NUMBER : 02 REVISION NUMBER : 2 DATE OF REVISION : February 8, 2002 DATE OF EXPIRING: February 8, 2005 FILE: GCTMP02-SALT CORROSION ¨C REV2.DOC WRITTEN BY : GLOBAL TEST TEAM MODIFIED BY : QPT TEAM APPROVED BY: SEGMENT PRODUCT LEADER: Martina M. Welcher REFERENCE: BRITISH STANDARD BS 7069 Appendix C. Corrosion- Modified (1) PURPOSE 目的 To provide a method for testing the corrosion resistance of non-stick coating systems. 用来测试不粘涂料的耐盐水腐蚀性。(2) PRINCIPLE 原理Exposure of coating systems to a boiling 10% NaCL (salt) solution for a total of 24 hours. 喷涂一指定涂料体系的锅子中，盛放10%的氯化钠（盐水）溶液，煮沸24 hrs。(3) APPARATUS 仪器3.1 Heat source 热源3.2 10% NaCL solution 10 %的氯化钠溶液3.3. De-ionized Water 去离子水(4) PREPARATION 准备4.1 Prepare test specimens in accordance to the procedure outlined on the product fact sheet for proper application, drying and baking of the specified Teflon. system. 按照产品技术说明书的程序要求正确准备测试样品，干燥并烘烤指定的特富龙涂料体系。4.2 Prepare 10% by weight, salt solution by combining 8 tablespoons (106 gr) Table Salt and 4 cups (960 gr) de-ionized water. 将8汤匙（106 gr）食盐溶解于4杯去离子水中以得到重量百分比10%的食盐溶液。4.3 Prepare a mild dish detergent solution with tap water. 用去离子水配备适度浓度的洗涤剂溶液。(5) PROCEDURE 程序5.1. Wash the test specimens in dish detergent solution. 用洗涤剂清洗测试样品。l Rinse in cold water. 冷水淋洗测试样品。l Dry thoroughly. 完全干燥。l Visually inspect coating surface for surface defects.用肉眼检查涂料表面缺陷。 l Draw a diagram of the test specimen surface. 用圆规画出测试面积表面草图。l Record all surface imperfections on the reference diagram. 在草图上标出所有的表面缺陷。5.2 Pour the 10% salt solution into the clean test specimen to a level past the midway point of the side wall of the vessel. 倒入10%的食盐水溶液于测试样品中，至少要达到其内壁一半的高度l Mark the water level on the side wall of the test specimen. 在测试样品内壁标注水面高度l Cover the test specimen with a lid. 盖上盖子。5.3. Place the test specimen on the heat source. Boil the solution for 24 hours. 将测试样品放在热源上，加热溶液24hrs。l Boil the solution for 24 hours. Add de-ionized water to maintain the water level within 15mm (6.6 inches) at all times.煮沸溶液24hrs。每隔一定时间（半小时左右）添加去离子水，以保持水面高度偏差在15mm(6.6 inches)以内。 l The 24 hour period may be continuous or, alternately, may comprise If the 8 hour interval is used, remove for the heat source safely. 24小时可以是连续，也可以间断进行。比如可以选用8小时一个循环，总共三个循环。煮完后安全地从热源上移开样品。l Pour the remaining liquid from the test specimen at the end of each cycle. 在最后的循环后倾倒样品中残留的盐水。5.4 Wash the test specimen in warm water using the mild dish detergent solution until adhering salt deposits are completely removed. 使用温和的洗涤剂在温水中清洗样品，直至残留的盐分完全洗掉。5.5 Visually examine the test specimens after each cycle for defects (blisters) not Present in the initial mapping. Record new defects on the reference diagram. 每一循环结束后用肉眼检查样品表面新的缺陷（水泡），并在参考草图上标注。5.6 Store the test specimens without liquid, dry, overnight. 放置无盐水的样品，干燥，过夜。5.7 Repeat the process until a complete 24 hours is completed. 重复程序，直到完成24hrs的测试时间。5.8 Visually examine test specimen for defects and record on reference diagram. 用肉眼检查样品表面的缺陷并记录在参考草图上。(6) EVALUATION 评价 6.1. Using the supplied Blister Rating Guide, compare the mapping diagram to the figures for the appropriate rating assessment. Record. 使用水泡评级指南来比较草图上的缺陷，得出合适的评级数。(7) REPORTING 报告 7.1. Report the blister rating including 报告水泡级别。7.2 Record the following information about the test specimen: 记录样品的下列信息：l Dry Film Thickness (DFT) 膜厚l Substrate and surface preparation 基材以及基材制备l Coating System 涂料体系l Manufacturer 厂商l Source 来源(8)PRECISION 精度The precision of the test has not been established. The test method and the rating system are subjective. Therefore it is recommended that for each set of experiments, the reproducibility is measured by including at least one reference (also called “standard” or control specimen) and data is gathered for each set separately . 精度无法得到，测试方法和评级体系是主观的。因此，对于每组测试，建议使用参照品（称之为标准样或受控样品）来衡量测试的重现性，并且分开纪录每组测试的数据。(9) DOCUMENTS 文档British Standard BS 7069 -1988. (10) Attachment 1: Blisters rating 水泡评分标准：RATINGNUMBER OF DESCRIPTION评级BLISTERS / dm2 状况描述OR / 15.5 inch2 （水泡数量/平方分米）50NONE无任何腐蚀4<1VERY SLIGHT非常轻微腐蚀3 1.1 - 2.0SLIGHT轻微2 2.1 - 3.0MODERATE中等1 3.1 - 5.0SEVERE严重0> 5.1VERY SEVERE非常严重.精品文档.DUPONT TEFLON. FINISHES GLOBAL COOKWARE TEST METHOD PROTOCOL
