各种塑料的材质性能参数-.pdf

编辑文本.附表 1：共 4 页第2 页序类型项目PA6PA6+15%GFPA6+20%GFPA6+30%GFPA66PA66+10%GFPA66+15%GFPA66+20%GFPA66+25%GFPA66+30%GF1密度g/cm31.12-1.161.3-1.41.24-1.281.34-1.41.12-1.161.16-1.221.22-1.261.3-1.41.320.051.32-1.42燃烧残余%28-328-1214-1620225327-353融化温度210-220210-220250-260250-260250-2602552554*熔融指数g/10min4-1030-605*抗拉强度N/mm28011515570901101306*屈服极限N/mm27*断裂伸长率%22.58球压硬度N/mm270-90 180205140 1601601801801959*冲击强度KJ/m220 30 4680253510*缺口冲击强度KJ/m25 79.52.546 611无缺口冲击强度KJ/m22512*弯曲强度N/mm219522085 1401701706516013*维卡耐热14*热变形210 编辑文本.注：所有项目为原材料进货时根据质保书对材料进行核查，带*号的项目为材料进货时对其性能进行的复检附表 2:共 4 页第3 页序类型项目PP2PP4PP6(PP+TD20)PP+TF30PP8(PP+TD40)PP9(PP+20%G F)PP10(PP+30%GF)PP+40%云母PP+PEPET聚酯弹性体1密度g/cm30.910.010.910.011.050.021.10.021.22 0.021.050.021.150.021.240.021.08 0.021.18-1.222燃烧残余%353融化温度158158158 1581581584*熔融指数g/10min6-105-105*抗拉强度N/mm2 30305034.525306*屈服极限N/mm2302430277*断裂伸长率%5008球压硬度N/mm2654880 8885751101209*冲击强度KJ/m2不碎不碎2010251510*缺口冲击强度KJ/m23.52.542.4711*弯曲强度N/mm240 554538703512*维卡耐热13*热变形 135210 编辑文本.注：所有项目为原材料进货时根据质保书对材料进行核查，带*号的项目为材料进货时对其性能进行的复检附表 3:共 4 页第4 页序类型项目PBTPBT+10%GFPBT+20%GFPBT+30%GFPPS+40%GFPCABSABS+PCHDPELDPEPOM1密度g/cm31.6-1.71.18-1.221.04-1.081.12 0.01 1.04-1.120.9-1.11.39-1.432燃烧残余%17-2328-323融化温度3034*熔融指数g/10min10-127-115*抗拉强度N/mm2 60 60 60 100 211 60 25 13586*屈服极限N/mm27*断裂伸长率%15280 60 500108球压硬度N/mm2 85 909*冲击强度KJ/m2 90 30不断9 010*缺口冲击强度KJ/m2 3.55 5.56307 20311*弯曲强度N/mm2 90 100 160 16090 656812*维卡耐热 150 150 190200 100 120 57 8513*热变形 编辑文本.注：所有项目为原材料进货时根据质保书对材料进行核查，带*号的项目为材料进货时对其性能进行的复检附表 2:共 4 页第3 页序类型项目POMGF10PPGF10PP-TD15（JC-T719-11密度g/cm31.590.02-2燃烧残余%3融化温度-4*熔融指数g/10min7-115*抗拉强度10040 N/mm26*屈服极限N/mm27*断裂伸长率%8球压硬度N/mm2-9*冲击强度KJ/m2 5 15 KJ/m210*缺口冲击强度KJ/m211*弯曲强度N/mm21206012*维卡耐热13*热变形 编辑文本.注：所有项目为原材料进货时根据质保书对材料进行核查，带*号的项目为材料进货时对其性能进行的复检