ASTM D2344 D2344M 聚合物基复合材料及其层压材料短梁强度的标准试验方法.docx

《ASTM D2344 D2344M 聚合物基复合材料及其层压材料短梁强度的标准试验方法.docx》由会员分享，可在线阅读，更多相关《ASTM D2344 D2344M 聚合物基复合材料及其层压材料短梁强度的标准试验方法.docx（2页珍藏版）》请在淘文阁 - 分享文档赚钱的网站上搜索。

1、ASTM D2344 D2344M聚合物基复合材料及其层压材料短梁强度的标准试验方法标准名称ASTM D2344 D2344M Standard Test Method for Short-Beam Strength of Polymer Matrix Composite Materials and Their LaminatesASTM D2344 D2344M聚合物基复合材料及其层压材料短梁强度的标准试验方法适用范围Scope:This test method determines the short-beam strength of high-modulus fiber-reinforc

2、ed composite materials. The specimen is a short beam machined from a curved or a flat laminate up to 6.00 mm 0.25 in. thick. The beam is loaded in three-point bending引用文件ASTM D792 Test Methods for Density and Specific Gravity (Relative Density) of Plastics by DisplacementASTM D883 Terminology Relati

3、ng to PlasticsASTM D2584 Test Method for Ignition Loss of Cured Reinforced ResinsASTM D2734 Test Methods for Void Content ofRe info reed PlasticsASTM D3171 Test Methods for Constituent Content of Composite MaterialsASTM D3878 Terminology for Composite MaterialsASTM D5229/D5229M Test Method for Moist

4、ure Absorption Properties and Equilibrium Conditioning of Polymer Matrix Composite MaterialsASTM D5687/D5687M Guide for Preparation of Flat Composite Panels with Processing Guidelines for Specimen PreparationASTM E4 Practices for Force Verification of Testing MachinesASTM E6 Terminology Relating to

5、Methods of Mechanical TestingASTM E18 Test Methods for Rockwell Hardness of Metallic MaterialsASTM E122 Practice for Calculating Sample Size to Estimate, With Specified Precision, the Average for a Characteristic of a Lot or ProcessASTM E177 Practice for Use of the Terms Precision and Bias in ASTM T

6、est MethodsASTM E456 Terminology Relating to Quality and StatisticsASTM E1309 Guide for Identification of Fiber-Reinforced Polymer-Matrix Composite Materials in DatabasesASTM E1434 Guide for Recording Mechanical Test Data of FiberReinforced Composite Materials in DatabasesASTM E1471 Guide for Identification of Fibers, Fillers, and Core Materials in Computerized Material Property Databases