1、1Literature source第1页/共21页2ContentsIntroduction 12 Experimental section1 Conclusions234Results and discussion第2页/共21页31.Introduction The shortage of traditional energy resources and serious environmentalpollution due to combustion emissions have resulted in a number of scientific studies on the deve

2、lopment of sustainable and clean energy,including fuel cells.第3页/共21页41.Introduction Methanol oxidation in a direct methanol fuel cell(DMFC)can generate electrochemical energy.DMFCS working principle:Cathode Polymer Anode membraneCO2H2OH2OCO2H2OO2H+：CH3OHe-e-Loadinge-CathodecatalystAnodecatalystWast

3、e heat Anode：CH3OH +H2O CO2+6H+6e-0=0.046V Cathode：3/2 O2 +6H+6e-3H2O 0=1.229V CH3OH+3/2 O2 CO2+2H2OE0=1.183V第4页/共21页 This oxidation usually needs a catalyst to lower the reaction barrier to make the process efficient.So far,platinum(Pt)is the most efficient catalyst in the field.Scarcity of Pt,whic

4、h causes its high cost,inevitably impedes the active development of both scientific research and practical utilization.The utilization of single-component Pt in DMFCs suffers from serious carbon monoxide(CO)poisoning.CO,one of the main intermediate molecules,can easily stain Pt atoms,which deteriora

5、tes their catalytic activity.5The article thought：In this study,we achieved higher catalytic activity for methanol oxidation using the perpendicular bimetallic Pt/Pd NT array as a catalyst.The investigation of the catalytic properties of bimetallic materials paves a way to substituting expensive Pt

6、with cost-competitive materials in the future.第5页/共21页6 Experimental section2第6页/共21页72.Experimental section5 mM PdCl25 mM H2PtCl640 mM HClused for depositionThe lengths of the NTs can be controlled by using 0.3 to 2 C.AAOa vertically-aligned bimetallic Pt/Pd nanotube arrayScheme 1 Schematic drawing

7、 of the ion distribution in a porous alumina nano-template.Dashed lines show the electrical double layer of the classical GouyChapmanSterns model between(b)diffusion layer and(c)bulk layer regions in a nanochannel.Region(a)depicts a compact layer.第7页/共21页823Results and discussion第8页/共21页93.Results a

8、nd discussion The average outer diameter and wall thickness of the Pt/Pd NTs were measured as 217(39 nm)and 37(12 nm),respectively.As shown in the SEM images,the resulting morphology of the nanostructures was quite homogeneous over a large area of the sample.Synthesis of bimetallic Pt/Pd nano-tubes

9、and morphology analysis第9页/共21页103.Results and discussionAs the Pt/Pd ratio increased(i.e.,the proportion of Pt4+increased),the nanostructures became rod shapes.As the Pt/Pd ratio decreased(i.e.,the concentration ofPd2+increased),the nanostructures gradually started to show an open nano-tubular(ONT)

10、shape.第10页/共21页113.Results and discussionWhen 5 mM Pd and 5 mM Pt precursor ions were in the plating solution,Pt49/Pd51 NTs could be preparedA plot of atomic%of Pt in Pt/Pd bimetallic nanostructures vs.amount of Pt source第11页/共21页123.Results and discussion(A)TEM image of Pt/Pd NTs with 1 C(2.4 0.4 m

11、m)shows the totally tubular structure from bottom to top.(B)TEM image of a Pt/Pd NT and line-scanning profiles in the radial direction,indicating Pt(red trace)and Pd(green trace)distributions.The corresponding elemental mapping images are shown for(C)Pt and(D)Pd.第12页/共21页133.Results and discussionFE

12、-SEM images(BSE mode)of the Pt/Pd NTs.The lengths of the Pt49/Pd51 NTs were tuned by using(A)0.3 C,(B)1 C and(C)2 C.(D)The Pt/Pd NTs have average lengths from 1.1 0.1 mm to 4.9 0.9 mm.第13页/共21页143.Results and discussion返回返回Electro-catalytic properties(A)Cyclic voltammograms(CVs)of Pt and/or Pd nanos

13、tructures withsame lengths(ca.2.4 mm)in 0.5 M H2SO4 solution at room temperature.As shown in Fig.A,the value of the surface charge of the Pt/Pd NT catalysts was found to be 1.7 times larger than that of the Pt/Pd NRs.第14页/共21页153.Results and discussion(B)Anodic striping of CO oxidation in 0.5M H2SO4

14、 aqueous solution for different catalysts(only the oxidative CO removal region is shown).The observed peak intensity of CO oxidation on the Pt/Pd NRs was two times higher than that of the pure Pt and Pd NRs.Interestingly,the onset potential of CO oxidation for the Pt/Pd bimetallic nanostructures(0.6

15、1 V)appeared at a lower potential compared tothe pure Pt NRs(0.69 V)and the pure Pd NRs(0.79 V).第15页/共21页163.Results and discussion(C)Cyclic voltammograms of methanol oxidation using different catalysts.The inset image shows the magnified onset potential region of the CVs.The Jf/Jb ratios of the Pt/

16、Pd NTs and Pt NRs were determined to be 1.6 and 1.2,respectively.The Vonset was found to be in the order:Pt/Pd NTs(0.42 V)Pt/Pd NRs(0.44 V)Pt NRs(0.49 V)第16页/共21页173.Results and discussion(D)Comparison of chronoamperograms of methanol oxidation for different catalysts at 0.4 V(vs.Ag/AgCl).Electrolyt

17、e for methanol oxidation:0.5 M H2SO4 and 0.2 M CH3OH solution at room temperature.Scan rate:50 mV s-1.We found that Pt/Pd NTs showed the highest current density compared to other nanostructures.第17页/共21页18 Conclusions4第18页/共21页194.conclusions1、We demonstrated a facile route to synthesize highly orde

18、red Pt/Pdbimetallic nano-tube electrodes based on an AAO template-directed electrochemical method.2、The perpendicular Pt/Pd bimetallic nano-tubes presented in this manuscript are potentially useful as enhanced electro-catalysts in methanol or other types of fuel cell.第19页/共21页20Thank you for your attention!第20页/共21页21感谢您的观看！第21页/共21页